From 27 to 30 September 2022, we will have a stand at the Micronora trade fair in Besançon, France, which is the largest micro technology exhibition in Europe. We would be delighted to welcome you to our stand to see and touch our actual μ-MIM parts. This is a joint stand with Incus GmbH, a manufacturer of metal 3D printers using the Lithography-based Metal Manufacturing (LMM) method. We look forward to seeing you there.
Date: 27-30 September 2022
Place: Parc des Expositions Micropolis / Boulevard Ouest, Besançon, France
Contact: Ms. Izumi Nakamura (firstname.lastname@example.org)
Cracking, slumping or blistering is commonly observed due to the binder swelling and/or residual stress difference between the surface and interior. It is possible to avoid these problems by selecting appropriate organic solvents and temperature control.
The catalytic deboning uses sublimation of binder, thus it is possible to decompose the binder in relatively short processing time with minimizing the deformation. However, with a strong acidic atmosphere, theapplicable metal material option is limited.
In the sintering process, the necking, which is bridging the metal powders by thermal diffusion, starts at the sintering temperature. Once the necking starts, the shrinking is observed and increases the density, thus before starting the necking reaction, all the organic components should be decomposed and gas between the powders should be removed. In the sintering process, the unwanted chemical reaction, such as oxidation or carbonization, leads to mechanical property loss, therefore a precise atmosphere control with low heating rate at the beginning of the process is required. Also, when it reaches the sintering temperature, some add it vegetal can be evaporated.